Material Specification (1)

 LITCHFIELD INTERNATIONAL MATERIAL SPECIFICATION SHEET NYLON 6 /6 Polymer TECHNYL A 205F ® HangerLok -­‐ #12, #71, #80 VYDYNE ® ECO-­‐315 HangerLok -­‐ #15, #17, #20, #22, #25, #28 #32, #36, #40, #47, #51, #59, #113 WHY NYLON 6/6 POLYMER? Nylon 6/6 polymer has a long history of use in various market and products. From Automotive to telecommunication products, the material has excellent durability, high mechanical strength, great rigidity, and good stability under heat. Nylon 6,6's longer molecular chain and denser structure qualifies it as a premium nylon fiber, specified most often by professional architects and designers for use in commercial settings HangerLoK “One Level Up” CUSTOMER SERVICE: 888.443.3999 ORDER FAX LINE: 877.349.7141 EMAIL ORDER TO: orders@litchfieldinternational.com TECHNICAL/ GENERAL INQUIRIES: info@hangerlok.com info@litchfieldinternational.com TECHNYL ® A 205F Properties Physical Mechanical Thermal Electrical Specifical Identification code Standards Unit Water absorption, 24h in water at 23°C ISO 62 % Density ISO 1183-­‐A g/cm3 Moulding shrinkage longitudinal RHODIA-­‐EP % Moulding shrinkage transverse RHODIA-­‐EP % Tensile Modulus ISO 527 MPa Yield stress ISO 527 MPa Elongation at yield ISO 527 % Stress at 50% elongation ISO 527 MPa Tensile stress at break ISO 527 MPa Nominal tensile strain at break ISO 527 % Flexural modulus ISO 178 MPa Flexural strength ISO 178 MPa Charpy notched impact strength ISO 179/1EA-­‐1993 Charpy notched impact strength ISO 179-­‐1982 kJ/m2 Charpy impact strength ISO 179/1EU-­‐1993 Charpy impact strength ISO 179/1D ISO 179-­‐1982 kJ/m2 Izod notched impact strength ISO 180 kJ/m2 Melt temperature ISO 3146 -­‐ C °C Temper. of dimensional stability 1,8 MPa ISO 75-­‐2 °C Coef. linear expansion longit. 23°C-­‐85°C ASTM E 831 E-­‐5 / °C Flammability UL94 thickness 0,4mm ISO 1210/UL 94 -­‐ Flammability UL94 thickness 0,8mm ISO 1210/UL 94 -­‐ Flammability UL94 thickness 1,6 mm ISO 1210/UL 94 -­‐ Glow wire test thickness 1,6 mm IEC 695-­‐2-­‐1 °C Relative permittivity 1MHz Dissipation factor 1 MHz Volume resistivity Surface resistivity Dielectric strength Comparative tracking index KC Comparative tracking index KB IEC 250 IEC 250 IEC 93 IEC 93 IEC 243-­‐1 IEC 112 IEC 112 Limit oxygen index ISO 4589 >PA66< -­‐ -­‐ E14.Ohm.cm E14.Ohm kV/mm Volt Volt % Values EH 0-­‐23°C EH 50-­‐23°C 1.2 1.14 1.9 1.9 -­‐ -­‐ -­‐ -­‐ 3200 85 4 -­‐ 60 25 2900 120 kJ/m2 5 kJ/m2 NB 4.5 1600 50 10 50 40 200 1300 50 4.5 15 NB NB 6 263 75 7 V2 V2 V2 850 -­‐ -­‐ -­‐ -­‐ -­‐ -­‐ 960 2.9 0.03 10 5 27 600 550 3.2 0.08 0.1 0.1 26 600 -­‐ 28.5 -­‐ VYDYNE ® ECO-­‐315 Properties Dry Unit Test Method Physical Density 1.16 g/cm3 ISO1183 Water Absorption @ 73°F 0.80 % ISO 62 Mechanical Tensile Modulus (73°F) Yield stress (73°F) Tensile Strain Yield 73°F Break 73 ° F Flexural modulus (73°F) Flexural strength (73°F) Poison’s Ratio Melt temperature (DSC) Heat Deflection Temperature 66 psi, Unannealed 264 psi, Unannealed Thermal Electrical psi psi 5.5 25 464000 13300 0.41 % % psi psi -­‐-­‐ Flame Rating 0.118 in, All colors ISO 527-­‐2 ISO 527-­‐2 ISO 178 ISO 178 ISO 527-­‐2 471 °F ISO 3146 437 °F ISO 75-­‐2/B 149 °F ISO 75-­‐2/A Volume Resistivity (0.118 in) Electric Strength 0.0394 in 0.118 in Arc Resistance (0.118 in) Comparative Tracking Index (CTI) (0.118in) Comparative Tracking Index (0.118 in) High Amp Arc Ignition 0.0591 in 0.118 in Hig Voltage Arc Tracking Rate (HVTR) Flammability 725000 10900 3.0E+15 ohm-­‐cm 670 V/mil 410 V/mil PLC 5 PLC 0 >600 PLC 0 -­‐-­‐ PLC 0 -­‐-­‐ PLC 1 -­‐-­‐ V-­‐0 -­‐-­‐ IEC 60093 IEC 60243-­‐1 ASTM D495 UL 746 IEC 60112 UL746 UL746 UL94