METRODE

Transcription

METRODE
METRODE
A18
WELDING CONSUMABLES
1NiMo.B
Product description
All-positional NiMo low alloy steel MMA electrode
MMA electrode with a basic flux coating on high purity mild steel core wire. Moisture resistant coating provides
very low weld metal hydrogen levels.
Recovery is about 120% with respect to core wire, 65% with respect to whole electrode.
Specifications
ASME IX Qualification
Composition
(weld metal wt %)
E9018-G
AWS A5.5
BS EN 757
Approvals
E 55 4 1NiMo B 32
TÜV, DNV
QW432 F-No 4, QW442 A-No 10
min
max
typ
C
Mn
Si
S
P
Cr
Ni
Mo
Cu
V
0.04
0.07
0.06
1.0
1.4
1.2
-0.5
0.3
-0.020
0.01
-0.025
0.01
-0.3
0.1
0.8
1.2
1.0
0.20
0.50
0.4
-0.10
0.05
-0.03
0.01
All-weld mechanical
properties
PWHT 590-620°C/1-2h:
min
Operating parameters
DC +ve or AC (OCV: 70V min)
typical
250°C
MPa
MPa
%
%
%
Tensile strength
0.2% Proof stress
Elongation on 4d
Elongation on 5d
Reduction of area
ø mm
min A
max A
620
530
17
---
720
645
26
23
65
High Temperature
350°C
450°C
650
505
22
-57
640
445
28
-69
2.5
3.2
4.0
5.0
70
110
80
140
100
180
140
240
Packaging data
ø mm
Storage
3 hermetically sealed ring-pull metal tins per carton, with unlimited shelf life. Direct use from tin will give
hydrogen < 5ml/100g for longer than a working shift of 8h.
For electrodes that have been exposed:
Redry 250 – 300°C/1-2h to ensure H2 < 10ml/100g, 300 – 350°C/1-2h to ensure H2 < 5ml/100g. Maximum
420°C, 3 cycles, 10h total.
Storage of redried electrodes at 50 – 150°C in holding oven or heated quiver: no limit, but maximum 6 weeks
recommended. Recommended ambient storage conditions for opened tins (using plastic lid): < 60% RH, > 18°C.
Fume data
Fume composition, wt % typical:
length mm
kg/carton
pieces/carton
2.5
3.2
4.0
5.0
350
12.9
546
350
13.5
369
450
16.8
240
450
18.0
171
545
432
24
-73
Fe
Mn
Ni
Cr
Cu
F
OES (mg/m3)
14
5
0.5
<0.1
<0.2
18
5
NET-LITE
TEL : +609-567 4662 FAX : +609-566 4459
EMAIL : sales@netlite.com.my
METRODE
A19
WELDING CONSUMABLES
MnMo
Solid MnMo low alloyed wire for TIG and MIG
Product description
Solid copper coated wire for TIG and MIG.
Specifications
AWS A5.28
BS EN 440
BS 2901: Pt1
ASME IX Qualification
QW432 F-No 6, QW442 A-No 11
Composition
(wire wt %)
All-weld mechanical
properties
min
max
typ
ER80S-D2, ER90S-D2
(G4Mo)
A31
C
Mn
Si
S
P
Ni
Mo
Cu
0.07
0.12
0.1
1.60
2.10
1.9
0.50
0.80
0.6
-0.025
0.005
-0.025
0.01
-0.15
0.05
0.40
0.60
0.5
-0.4
0.1
Typical values PWHT
590-620°C/1-2h
min *
MPa
MPa
%
J
HV
Tensile strength
0.2% Proof stress
Elongation on 4d
Impact energy
- 30°C
Hardness cap/mid
550
470
17
27
--
TIG
MIG
640
530
32
200
235/210
Ar +
5%CO2
Ar +
20%CO2
725
625
28
>100
235/220
High Temperature (TIG)
250°C
350°C
450°C
605
490
25
>100
220/205
650
525
24
---
665
490
27
---
585
460
25
---
* Minimum as-welded values are for AWS ER80S-D2. As shown MAG welds using more oxidising shielding gas
(higher CO2 + O2) have lower strength. The AWS classification for ER80S-D2 is based on 100%CO2 which is
seldom used; alternatively this wire can also be classified as ER90S-D2 using low CO2 gas mixtures.
Typical operating
parameters
TIG
*
MIG
Argon
DC2.4mm
120A, 14V
Shielding
Current
Diameter
Parameters
Ar + 5-20%CO2 *
DC+
1.2mm
280A, 26V
Ar + 5%CO2 provides the highest strength and best impact properties, see above. Other proprietary gas
mixtures also suitable.
Packaging data
ø mm
Fume data
MIG fume composition (wt %) (TIG fume negligible)
1.2
1.6
2.0
2.4
3.2
TIG
MIG
-5kg tube
5kg tube
5kg tube
5kg tube
15kg spool
-----
Fe
Mn
Cr3
Ni
Mo
Cu
OES (mg/m3)
55
10
<0.1
<0.1
<0.5
1.2
5
NET-LITE
TEL : +609-567 4662 FAX : +609-566 4459
EMAIL : sales@netlite.com.my
METRODE
A20
WELDING CONSUMABLES
SA1NiMo
Solid NiMo alloyed wire for SAW
Product description
Solid copper coated wire for submerged arc welding. Nominal composition of 1%Ni-0.5%Mo capable of achieving
90ksi (620MPa) tensile strength. Supplied to NACE MR0175 1.0%Ni maximum on request.
Specifications
AWS A5.23
BS EN 756
ASME IX Qualification
QW432 F-No 6, QW442 A-No 10 (Nearest)
Composition
(wire wt %)
min
max
typ
EF3
S3Ni1Mo
C
Mn
Si
S
P
Ni *
Mo
Cr
Cu
0.08
0.15
0.10
1.30
2.40
1.75
0.05
0.25
0.2
-0.020
0.005
-0.020
0.01
0.8
1.2
0.9
0.45
0.65
0.55
-0.20
0.05
-0.30
0.1
* Ni supplied to 1.0% maximum (NACE MR0175) on request.
All-weld mechanical
properties
Typical operating
parameters
Packaging data
Fume data
Typical values as-welded & PWHT
Tensile strength
0.2% Proof stress
Elongation on 4d
Impact energy
MPa
MPa
%
J
+20°C
AW
590°C/2h
700
600
20
90
680
560
28
140
SAW
LA436 flux
DC+
2.4mm
450A, 30V, 450mm/min
Shielding
Current
Diameter
Parameters
ø mm
SAW
25kg coil
25kg coil
25kg coil
25kg coil
1.6
2.4
3.2
4.0
To order
Fume composition (wt %) (SAW fume negligible)
Fe
Mn
Cr3
Ni
Mo
Cu
OES (mg/m3)
50
10
<0.5
<0.5
<1.5
1.2
5