Eurogel GCP / GCTC 500 Series Iso-modified

Eurogel GCP / GCTC 500 Series Iso-modified
Brush
Eurogel GCP-512 AD (auto-démoulant)
Spray
Eurogel GCTC-512
Spray
Eurogel GCTC-511
Spray
Eurogel GCTC-522
Brush
Eurogel GCTC-521
Brush
For further information please refer to Products & Applications pages:
•
•
•
•
euromere.com
Density
Eurogel GCP-522
•
•
•
Gel time / min (on 200gr mass,
at 20°C, 1% MEKP 50)
Spray
Thix. Index
Eurogel GCP-512
Viscosity / poises
Application
Topcoat
Reference
In mold
Applications : Industrial, Transportation, Building, General purpose. Standard quality gelcoat, with stable storage and application properties.
Good protection for polyester laminates under outdoor conditions. Answer all demanding process requirements.
120-170
≥4
10-20
1,25
400-450
≥4
10-20
1,25
90-150
≥4
10-20
1,25
120-170
≥4
10-20
1,25
120-170
≥4
25-30
1,25
400-450
≥4
10-20
1,25
400-450
≥4
25-30
1,25
Eurogel GCP / GCTC 600 Series 100% isophtalic
Spray
Eurogel GCTC-611
Spray
Eurogel GCTC-622
Brush
Eurogel GCTC-621
Brush
For further information please refer to Products & Applications pages:
•
•
•
•
HDT / °C
Eurogel GCTC-612
Elongation at break
%
Brush
Flexural modulus
MPa
Eurogel GCP-621
Flexural strength
Mpa
Brush
Tensile modulus
MPa
Eurogel GCP-622
Tensile strength
Mpa
Spray
Density
Eurogel GCP-611
•
•
•
•
Gel time / min (on 200gr
mass, at 20°C, 1% MEKP 50)
Spray
Thix. Index
Eurogel GCP-612
Viscosity / poises
Application
Topcoat
Reference
In mold
Applications : Marine, Sanitary and Kitchen wares, Industrial, Transortation, Building.
Special formulation to answer the most demanding outdoor end product requirements. High properties of hydrolysis resistance.
120-170
≥5
15-20
1,1
80
3300
130
3400
4
90
120-170
≥5
25-30
1,1
80
3300
130
3400
4
90
400-450
≥5
15-20
1,1
80
3300
130
3400
4
90
400-450
≥5
25-30
1,1
80
3300
130
3400
4
90
120-170
≥5
15-20
1,1
80
3300
130
3400
4
90
120-170
≥5
25-30
1,1
80
3300
130
3400
4
90
400-450
≥5
15-20
1,1
80
3300
130
3400
4
90
400-450
≥5
25-30
1,1
80
3300
130
3400
4
90
euromere.com
Cured base resin properties
Eurogel HQ-212 / HQ-212 TC Series Iso-NPG
Spray
Eurogel HQ-222
Brush
Eurogel HQ-221
Brush
Eurogel HQ-212 TC
Spray
Eurogel HQ-211 TC
Spray
Eurogel HQ-222 TC
Brush
Eurogel HQ-221 TC
Brush
•
•
•
•
For further information please refer to Products & Applications pages:
Density (± 0,5)
Eurogel HQ-211
Gel time / min (on 200gr mass, at
20°C, 1% MEKP 50)
Spray
Thix. Index
Eurogel HQ-212
Viscosity / poises
Application
120-180
≥5
20-30
1,3
120-180
≥5
35-45
1,3
350-500
≥5
20-30
1,3
350-500
≥5
35-45
1,3
120-180
≥5
20-30
1,3
120-180
≥5
35-45
1,3
350-500
≥5
20-30
1,3
350-500
≥5
35-45
1,3
Topcoat
Reference
In mold
Applications : Marine, Swimming-pool, Spa, Industrial, Transportation, Building.
Very high resistance to hydrolysis, UV radiations, and in marine environment.
•
•
•
•
euromere.com
Eurogel GCP 800 Series 100% vinylester
Tensile strength Mpa
Tensile modulus MPa
Flexural strength Mpa
Flexural modulus MPa
Elongation at break %
HDT / °C
Spray
Density (± 0,5)
Eurogel GCP-811
•
•
Gel time / min (on 200gr mass, at
20°C, 1% LPT)
Spray
Thix. Index
Eurogel GCP-812
Viscosity / poises
Application
120-170
≥5
10-15
1,1
72
3600
130
3700
2
135
120-170
≥5
15-30
1,1
72
3600
130
3700
2
135
Topcoat
Reference
In mold
Applications : Moulds, tanks
Good resistance to temperature and chemical products. High gloss and hardness.
Standard colours : green, black, transparent.
For further information please refer to Products & Applications pages:
euromere.com
Cured base resin properties
Eurogel - Specific Topcoats
13-20
Eurogel GCTC-312
Brush/Roller
•
230-280
≥5
(2% PMEC50,
at 20°C on 200gr)
Eurogel GCTC-313
Brush/Roller
•
230-280
≥5
(2% PMEC50
at 20°C on 200gr)
Eurogel GCTC-1201
Brush/Roller
•
170-250
2,5-4
(1% PMEC50,
at 20°C on 200gr)
Eurogel LP-TC 1201
Brush/Roller
•
170-250
3-5
(2% PMEC50,
at 23°C, on 100gr)
Eurogel GCTC-10089
Brush/Roller
•
300-500
4-6
(2% PMEC50,
at 23°C on 200gr)
For further information please refer to Products & Applications pages:
8-15
35-45
50-70
euromere.com
10-15
Density (± 0,5)
Geltime / min (on mass)
Thix. Index
Viscosity / poises
Application
Topcoat
Reference
Mold
Answer specific Top Coating requirements
Applications : Marine, Transportation, Building, Wind-, Tank- and Other industries…
(Refer to Eurogel 500, 600, HQ and 800 for our standard topcoats)
Comments
1,2
Very High surface tension. Satin/Gloss surface finish. High
covering power.
Possible to apply with one coat only according to support surface
quality.
Also possible to apply with 2 coats without sanding between
layers.
1,2
Higher reactivtiy version of GCTC-312.
1,5
Higher covering power. Possible to apply with only one coat.
Satin/Gloss surface finish. Air release additive included.
High cost/performance ratio.
1,35
Long gel time, higher thix index, superior covering power. Only
one coat possible. Satin/Gloss surface finish. Air release additive
included.
High cost/performance ratio.
1,38
Top Coat with anti skid properties (sand) for truck flooring
construction. High covering power and abrasion resistance.
Eurogel - Products for repairs / High thixotropic paste
Thix. Index
Geltime / min
(at 20°C, on 200 gr mass,
1% of PMEC50)
Density (± 0,5)
Brush/Spatula
•
3000-6000
≥7
15-20
1,1
High viscosity top coat. Fairing putty based on iso resin for
finishing repair job. Good mechanical properties. High gloss.
Eurogel HQRTC
Brush/Spatula
•
5000-10000
>8
_
1,3
High viscosity top Coat. Fairing putty based on isoNPG resin for
finishing repair job. Good mechanical properties, high gloss.
Pâte FT-711 Incolore
Brush/Spatula
5000-10000
≥7
30-60
1,1
High thixotropic paste. Specially developped to increase polyester
gel coat thixotropy for making it usable by hand application (eg.
Joint plane). High water resistance and gloss and color retention.
Application
Topcoat
Eurogel GCRTC
Reference
Mold
Viscosity / poises
Applications : all industries- Marine, Sanitary, Swimming-Pool, Transportation, Building, Wind, Tank
(For in mold repair application, refer to Eurogel 500, 600, HQ and 800 brush versions ranges )
•
For further information please refer to Products & Applications pages:
euromere.com
Comments
Gel time / min (on
130gr mass, at 20°C,
2% MEKP 50)
Density (± 0,05)
Application
Thix. Index
Reference
Viscosity / poises
FSP-SC > Sprayable core material, thick and lightweight topcoat
Comments
FSP-SC 1527
Spray
550-700
≥5
0,7
15-20
Application in sandwich construction, to replace fiberglass, felt, foam, and other core materials.
High mechanical properties, high rigidity, no water uptake.
Significant time savings, no roll, application up to 5mm in vertical without sagging.
Improved surface quality (low exotherm, low shrink, fiber-marking reduction)
Low styrene content.
FSP-TC 1560
Spray
500-650
3,5
0,7
15-25
Application as a thick top coat, to fill the surface defects of laminates.
Good surface tension.
Can be laminated over without sanding.
For further information please refer to Products & Applications pages:
euromere.com
FSP-BC 1701/300
Brush
FSP-BC 1700
Spray
FSP-BC 1700 T
Spray
FSP-BC 1101
Spray
•
•
•
Density (±0,5)
Spray
Time before over
lamination / min
FSP-BC 1701
•
•
•
Gel time / min (on 130gr
mass, at 20°C, 2% MEKP
50)
Spray
Thix. Index
FSP-BC 1701 T
Viscosity / poises
Application
100% vinylester base
Reference
Iso-Vinylester base
Protective coat directly applied behind gelcoat, to replace the first layer of laminated skin coat generally done with Iso or VE resin + fiberglass.
180-220
≥5
15-25
45
0,8 ± 0,05
High thixotropy
80-100
≥4
8-12
30
0,8 ± 0,05
Low viscosity, high reactivity
280-320
≥4
15-25
45
0,8 ± 0,05
High viscosity, for hand application
80-100
≥4
10-20
45
0,8 ± 0,05
Low viscosity, high reactivity
180-220
≥5
10-15
45
0,8 ± 0,05
High thixotropy
130-160
≥ 5,5
10-15
45
1,15 ± 0,05
Special version for robot spraying.
For further information please refer to Products & Applications pages:
euromere.com
Comments
Viscosity / poises
Thix. Index
Density (± 0,05)
Gel time / min (on 130gr mass,
at 20°C, 2% MEKP 50)
Exothermic peak / °C (± 10°C)
Bonding pastes, Putties, anti-bubble/radius compounds, cavity fillers.
2300-2800
≥5
0,6
15-30
150
3000-3500
≥8
0,8
15-30
Core material bonding (PU & PVC foams, balsa, etc). Medium reactivity.
Smooth to apply. Polyvalent product.
3000-3500
≥8
0,8
40-55
Core material bonding (PU & PVC foams, balsa, etc). Low reactivity.
Smooth to apply. Polyvalent product.
3300-3800
≥8
0,8
60-80
Anti-bubbles and bonding paste, very low reactivity. Smooth to apply.
Ideal for big parts and before injection.
5200-6000
≥7
1,3
15-30
Bonding paste, for balsa, PU & PVC foams, etc. Smooth to apply.
Medium reactivity. Low shrink. Fast version available.
5200-6000
≥7
1,3
6-12
Bonding-paste, similar to 1537, with higher reactivity.
15000-20000
≥ 5,5
1,33
25-40
Fibre-reinforced bonding paste. Good flexibility and low shrink. Smooth to apply. High
thixotropy for thickness application. Fast version available.
15000-20000
≥ 5,5
1,33
6-12
Fibre-reinforced bonding paste, similar to 1538 with higher reactivity.
4000-5000
≥ 6,5
1,1
40-65
FSP-HV 1534
FSP-HV 1535
FSP-HV 1590
FSP-HV 1537
FSP-HV 1537 S
FSP-HV 1538 FIBRE
FSP-HV 1538 S FIBRE
FSP-VE 9000
•
•
•
•
•
•
•
•
•
Cavity filling
FSP-HV 1528
Anti-bubble
Reference
Bonding paste
Application
•
•
•
•
•
•
•
•
•
For further information please refer to Products & Applications pages:
euromere.com
120
Comments
Low density product, high rigidity, no water uptake.
Application in high thickness. Polyvalent product.
100% vinlyester non-filled bonding paste, for high performance structural bondings.
Hand or machine application.
RESIMER 400 Series, Orthophtalic base
Gel time / min (on 200gr mass,
at 20°C, 1% MEKP 50)
Exothermic peak / °C ± 10°C
Tensile strength Mpa
Flexural strength Mpa
Flexural modulus MPa
Elongation at break %
HDT / °C
Resimer 400 HK
Density (±0,05)
Resimer 400
Viscosity / poises
Thixotroped
Reference
Accelerated
Good mechnical properties and heat resistance, excellent wetting properties, for general purpose applications.
2,5-3,5
1,1
8-11*
160
65
100
4200
1,5
80
Medium reactivity
5-7
1,1
8-11*
160
65
100
4200
1,5
80
Medium reactivity, for tropical climate.
Comments
Resimer 411
• •
15-25
1,1
35-40
125
65
100
4200
1,5
80
Adapted to warm seasons
Resimer 411 S
• •
15-20
1,1
25-30
(3% de PMEC)
140
65
100
4200
1,5
80
Lightly accelerated, tropicalized.
Resimer 411 Blanche
• •
15-25
1,1
35-40
125
65
100
4200
1,5
80
Adapted to warm seasons
Resimer 412
• •
15-25
1,1
20-30
140
65
100
4200
1,5
80
Winter version
Resimer 412 Blanche
• •
15-25
1,1
20-30
140
65
100
4200
1,5
80
Winter version
* with addition of 0,5% of cobalt (solution at 6%) in the resin
For further information please refer to Products & Applications pages:
euromere.com
RESIMER 500 Series, orthophtalic base, Low Styrene Emission
Reference
Accelerated
Thixotroped
Viscosity / poises
Density (±0,5)
Gel time / min (sur masse de
200gr, à 20°C, 1% PMEC 50)
Exothermic peak / °C ± 10°C
Tensile strength Mpa
Flexural strength Mpa
Flexural modulus MPa
Elongation at break %
HDT / °C
Low styrene content and low reactivity, for spray up application in high thickness.
Resimer 511
Bleue
•
•
22-27
1,1
65-80
125
65
100
4200
1,5
80
Blue resin with high thix. for good application
properties in vertical. Controlled exothermic peak.
Low reactivity.
Resimer 512
Bleue
•
•
18-22
1,1
50-70
125
65
100
4200
1,5
80
Blue resin with high thix. for good application
properties in vertical. Controlled exothermic peak.
High reactivity.
For further information please refer to Products & Applications pages:
euromere.com
Comments
RESIMER 600 Series, isophtalic base
Density (±0,5)
Gel time / min (on 200gr mass,
at 20°C, 1% MEKP 50)
Exothermic peak / °C ± 10°C
Tensile strength Mpa
Tensile modulus MPa
Flexural strength Mpa
Flexural modulus MPa
Elongation at break %
HDT / °C
Resimer 600
Viscosity / poises
Thixotroped
Reference
Accelerated
Good mechanical properties, good resistance to hydrolysis and chemical products. High wetting properties.
Good storage stability.
For laminates requiring high mechanical performance.
5-7
1,1
8-12*
190
80
3300
130
3400
4
90
Medium reactivity
Comments
Resimer 611
•
•
9-11
1,1
35-45
135
80
3300
130
3400
4
90
Medium reactivity, adapted to warm and wet
environments
Resimer 611 S
•
•
9-11
1,1
25-30
(3% de PMEC)
135
80
3300
130
3400
4
90
Tropicalised resin, better storage stability
Resimer 612
•
•
9-11
1,1
20-30
110
80
3300
130
3400
4
90
Winter version (high reactivity)
* with addition of 0,5% of cobalt (solution at 6%) in the resin
For further information please refer to Products & Applications pages:
euromere.com
RESIMER 800 Series, 100% vinylester base
Accelerated
Thixotroped
Viscosity / poises
Density (±0,5)
Gel time / min (sur masse de 200gr,
à 20°C, 1% PMEC 50)
Exothermic peak / °C ± 10°C
Tensile strength Mpa
Tensile modulus MPa
Flexural strength Mpa
Flexural modulus MPa
Elongation at break %
HDT / °C
Excellent mechanical and chemical resistance. Good resistance to corrosion and hydrolysis.
For high performance applications.
Resimer 811
•
•
9-11
1,1
35-45
150
72
3600
130
3700
2
135
Low reactivity
Resimer 812
•
•
9-11
1,1
15-25
150
72
3600
130
3700
2
135
High reactivity
Reference
For further information please refer to Products & Applications pages:
euromere.com
Comments
Viscosity / poises
Density (±0,5)
Thix. index
Gel time / min (on 130gr mass, at
20°C, 2% MEKP 50)
Exothermic peak / °C
Casting resins
MDC-LP
250-350
0,8
≥ 2,5
15-25
± 70
Low density, good casting properties, low shrink close to 0.
Sans charge abrasives.
MDC-17880
180-200
1,13
≥3
15-20
± 75
Low shrink, good reproduction of details, no abrasive fillers.
Ideal for rotomoulding process.
Reference
For further information please refer to Products & Applications pages:
Comments
euromere.com
Reference
Application
Viscosity / poises
Thix. Index
Density (± 0,05)
Gel time / min (on
130gr mass, at 20°C,
2% MEKP 50)
FSP-NR > No-roll lightweight product
FSP-NR 1556
Spray
2300-2800
≥5
0,9
15-30
For further information please refer to Products & Applications pages:
euromere.com
Comments
Lightweight product, for no-roll spray up application (simultaneous spray with
fiberglass).
Fast cure, low shrink and exotherm.
Improved productivity.
For further information please refer to Products & Applications pages:
Density (±0,5)
Spray
Time before over
lamination / min
FSP-BC 1700 T
•
•
Gel time / min (on 130gr
mass, at 20°C, 2% MEKP
50)
Spray
Thix. Index
FSP-BC 1700
Viscosity / poises
Application
100% vinylester base
Reference
Iso-Vinylester base
Barrier-Coat : Protective coat applied directly behind gelcoat, to replace the first layer of laminated skin coat generally done with VE or Iso resin + fiberglass.
80-100
≥4
10-20
45
0,8 ± 0,05
Low viscosity, high reactivity.
180-220
≥5
10-15
45
0,8 ± 0,05
High thixotropy
euromere.com
Comments
Reference
Application
Base
Viscosity / poises
Thix. Index
Gel time / min (on 100gr mass, at
20°C, 2% MEKP 50)
Density (±0,5)
Shore D Hardness
HDT / °C in film
CNC > Tooling pastes for CNC-machined plugs and models
CNC-2002 HS
Hand / Extrusion
Polyester
7000-12000
>6
120-240
1,1
70-75
45
Low reactivity, specially adapted to thick single layer
application, by extrusion, with drum pump equipment
(viscous product equipment).
CNC-3000 LG
Spray
Polyester / VE
400-550
>3,5
3-8
0,6
68
60
Hybrid base, higher hardness and heat resistance.
For further information please refer to Products & Applications pages:
euromere.com
Comments
Reference
Application
Viscosity / poises
Thix. Index
Gel time / min (on 250gr mass, at
20°C, 2% MEKP 50)
Density (± 0,05)
EUROLAQUE BLANCHE
Brush or spray
70-100
≥ 4,5
15-20
1,25
For further information please refer to Products & Applications pages:
euromere.com
Comments
White polyester laque for the finishing of plugs, moud refit, or various
topcoat uses. Easy to sand. High gloss. Good aging properties.
Eurogel GCP 800 Series, 100% vinylester base
Tensile strength Mpa
Tensile modulus MPa
Flexural strength Mpa
Flexural modulus MPa
Elongation at break %
HDT / °C
Spray
Density (± 0,5)
Eurogel GCP-811
•
•
Gel time / min (on 200gr mass, at
20°C, 1% LPT)
Spray
Thix. Index
Eurogel GCP-812
Viscosity / poises
Application
120-170
≥5
10-15
1,1
72
3600
130
3700
2
135
120-170
≥5
15-30
1,1
72
3600
130
3700
2
135
Topcoat
Reference
In mold
Applications : Moulds, tanks
Good resistance to temperature and to chemical products. High gloss and hardness.
Standard colours : green, black, transparent.
For further information please refer to Products & Applications pages:
euromere.com
Cured base resin properties
PRIMER 1206
Pot gun / Machine
80-100
≥4
20-30
60
Density (± 0,05)
Can be sanded after / min
Gel time / min (on 200gr mass, at
20°C, 1% MEKP 50)
Application
Thix. Index
Reference
Viscosity / poises
Polyester primers for the finishing of models and plugs, and preparing of metal parts before painting.
Comments
1,25
Easy to sand, low paper clogging.
Good surface appearance, no porosité, satin finish.
Allows a fast repair of surface defects.
Low styrene emission.
PRIMER 1202
Machine
70-80
≥4
3-6
30-45
1,15
Very high reactivity.
Fast dry.
Very good surface tension.
Enables thinner layers.
Easy to sand. Low paper clogging..
Excellent adhesion to cast iron and other metals.
Resistant to corrosion.
Low styrene content.
PRIMER 5000
Hand
4500-5500
≥ 4,5
5,8
45-60
1,5
Finishing primer for hand application, to fill, or repair surfaces before
painting. Catalyze with MEKP 50. Fast cure. Easy sanding. High rigidity and
HDT.
For further information please refer to Products & Applications pages:
euromere.com
RESIMER 800 Series, 100% vinylester base
Excellent mechanical and chemical resistance. Good resistance to corrosion and hydrolysis.
RESIMOLD Series
Accelerated
Thixotroped
Viscosity / poises
Density (±0,5)
Gel time / min (on 200gr mass, at
20°C, 1% MEKP 50)
Exothermic peak / °C ± 10°C
Tensile strength Mpa
Tensile modulus MPa
Flexural strength Mpa
Flexural modulus MPa
Elongation at break %
HDT / °C
Fast moulding system with very low shrink.
Resimer 811
•
•
9-11
1,1
35-45
150
72
3600
130
3700
2
135
Low reactivity
Resimer 812
•
•
9-11
1,1
15-25
150
72
3600
130
3700
2
135
High reactivity
Resimold
•
•
65-80
1,3
15-20
(1,5% MEKP50)
180
85
1,8
100
Low shrink resin for mould production. Fast
process. Excellent dimensional stability.
Reference
For further information please refer to Products & Applications pages:
euromere.com
110
Comments
FSP-SC 1527
Spray
550-700
≥5
For further nformation please refer to Products & Applications pages:
0,7
Gel time / min (on
130gr mass, at 20°C,
2% MEKP 50)
Density (± 0,05)
Application
Thix. index
Reference
Viscosity / poises
FSP-SC > Sprayable core material
15-20
euromere.com
Comments
Application in sandwich construction, to replace fibreglass, felt, foam, and other core
materials.
High mechanical properties, high rigidity, no water uptake.
Significant time savings, no roll, application up to 5mm in vertical without sagging.
Improved surface appearance (low exotherm, low shrink, reduction of fiber-marking)
Low styrene content.
TR Industries : Release agents and mould care products.
Référence
Description
Conditionnement
TR 104
Wax release, with high temperature resistance
Boite de 400 gr
TR 214
Mold cleaner - Liquid, without toluene, for cleaning and reuse wax
1 Gallon
TR 315
Strong polish compound, fast elimination of scratches and other surface defects. Can be followed with
TR-311 to reach a high quality finishing with high gloss.
1 Gallon
TR 900
Semi-permanent liquid agent
1 Gallon
TR 905
Cleaning solvent - very high cleaning power
1 Gallon
TR 910
Semi-permanent liquid sealer
1 Gallon
TR 940
One shot sprayable semi-permanent liquid agent
1 Gallon
For further information please refer to Products & Applications pages:
euromere.com