PRODUCT DATA SHEET
PETLIN
PETLIN LD MOSOX
Low Density Polyethylene
PETLIN LD MOSOX is a low density polyethylene resin designed primarily for injection moulding applications.
It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free)
additives.
flq~
high gloss, high filler acceptance.
.
Characteristics
low gels, high
Applications
lids, housewares, masterbatches; powder coating.
Extrusion Conditions
for injection moulding : recommended melt temperature 180-210°C.
Typical Data
Properties
Pol~mer
Units
Typical values
dg/min
kg/m 3
50
919
ISO 1133
ISO 1183 (A)
Test methods
grogerties :
Melt Flow Rate:
Density
Me!;hani!;gl
gro12erti~s
:
Hardness Shore D
43
ISO 868
Stress at yield
~tress at break
Strain at break
Modulus of elasticity
N/mm2
N/mm2
%
N/mm 2
8
7
200
168
ISO
ISO
ISO
ISO
Creep modulus
after 1 hr
after 1000 hr
N/mm 2
N/mm 2
73
38
Notch impact strength (Izod)
at 23°C
at -30°C
kJ/m2
kJ/m2
41
5
oc
oc
78
104
ISO 306
DIN 53765
hr
0.5
DSM Method
R527-2
R527-2
R527-2
R527-2
ISO 899
ISO 180/1A
Thermal grogerties :
Vicat Softening Temperature
Melting Point (DSC)
Misc. 12rogerties :
ESCR
The properties shown above are typical values and are not to be taken as specifications.
Food contact approval status :
This material complies with FDA 21 CFR 177.1520 when used unmodified and according to good
manufacturing practices for food contact applications. Accordingly, this material may be used in all food
contact applications (except holding food during cooking).
IMPORTANT NOTICE :
Information contained in this document is accurate and reliable to the knowledge and belief of Petlin (Malaysia) Sdn Bhd. The suggestions and
recommendations are offered herein as a guide in the use of Petlin products, and cannot be guaranteed because the conditions of use are beyond Petlin's
control. Petlin assumes no responsibility for the use of infonmation supplied, the application, adaptation or processing of its products described herein and
hereby disclaims all liability in regard to such use.
20040608 Version no. : 03
PETLIN {MALAYSIA) SON
BHD(478535-T)
PET LIN
PRODUCT DATA SHEET (PRELIMINARY)
PETLIN LD C150Y
Low Density Polyethylene
PETLIN LD C150Y is a low density polyethylene resin for general purpose and thin film applications. It
is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains slip, antioxidant
(BHT free) and antiblack additives. It is intended primarily for blown film process.
Characteristics: low gels, high drawdown, high clarity, high gloss, good sealability, high slip, high
antiblocking.
Applications: thin gauge films for textile, laundry, dry cleaning, garment; crosslinked foams; zip bags.
Recommended gauges : 15 - 60 microns.
Extrusion conditions : for blown film: melt temperature 145-165 oc and blow-up-ratio of 2 to 3: 1 are
recommendable.
Typical Data : ( 25 micron blown film}
Proeerties
Units
Polymer ~ro~erties:
Melt Flow Rate :
dg/min
Density
kg/m 3
TY.eical value
Test methods
5
921
ISO 1133
ISO 1183 (A)
62
7.2
ASTM 02457
ASTM D1003A
15
30
80
15
27
>450
100
190
190
0.2
ASTM 04272
ISO 6383-2
O~tical ~ro~erties:
Gloss (45°)
Haze
Mechanical ~ro~erties:
Impact strength
Tear strength
Tensile stress at break
Strain at break
Modulus of elasticity
Coefficient of friction
%o
%
TO
MD
TO
MD
TO
MD
TO
MD
kJ/m
kN/m
kN/m
MPa
MPa
%
%
MPa
MPa
ISO R527-1
ISO R527-1
ISO R527-1
Petlin method
The properties shown above are typical values and are not to be taken as specifications.
IMPORTANT NOTICE
Information contained in this document is accurate and reliable to the knowledge and belief of Petlin (Malaysia) Sdn Bhd. The suggestions
and recommendations are offered herein as a guide in the use of Petlin products, and cannot be guaranteed because the conditions of use
are beyond Petlin's control. Petlin assumes no responsibility for the use of information supplied, the application, adaptation or processing of
its products described herein and hereby disclaims all liability in regard to such use.
20010820 version no. : 01
ENVIRONMENT
The environmental aspects of any packaging material do not only imply waste issues but have to be
considered in relation with the use of natural resources, the preservations of foodstuffs etc. Petlin
considers polyethylene to be an environmentally efficient packaging material. Its low specific energy
consumption and insignificant emissions to air and water designate polyethylene as the ecological
alternative in comparison with the traditional packaging materials.
Petlin LD low density polyethylene, as supplied, can be recycled, incinerated or disposed of in landfill
without detriment to the environment.
The recycling of packaging materials is supported by Petlin whenever ecological and social benefits
are achieved . Whenever 'thermal' recycling of packaging (i.e. in~ineration with energy recovery) is
carried out, polyethylene - with its fairly simple molecular structure and low amount of additives - is
considered to be a trouble-free fuel.
SAFETY
Under normal conditions, polyethylenes do not present a toxic hazard through skin contact or
inhalation. During processing, contact with molten polymer and inhalation of volatile fumes should be
avoided. It is recommended to install exhaust hoods over processing machines and to keep working
area well ventilated. More specific information on the safety aspects of the Petlin LD low density
polyethylene is provided in the relevant Material Safety Data Sheets, available from Petlin's sales
agents.
STORAGE
As polyethylenes, like most polymers, are combustible, the usual precautions concerning ignition
sources should be taken in warehouses and storage rooms. It is necessary to observe the normal
rules for orderly and safe handling and to keep out dust, direct sunlight and moisture.
Further information is available from :
PETLIN (MALAYSIA) SON BHD
(478535-T)
Level 14, Tower 1, PETRONAS Twin Towers
Kuala Lumpur City Centre
50088 Kuala Lumpur,
Malaysia
1102K
P ol ypr op yl en e ( P P)
Description:
1102K is a Polypropylene Homo-polymer resin for extrusion process with the characteristic
of good stiffness and good impact. It is suitable for mono-filament and yarn, too. It also
meets the F.D.A. requirement in the code of federal regulations in 21 CFR 177.1520 for
food contact.
Typical applications;
Physical Properties:
Method
Unit
Value
Melt Flow Index (2.16 kg/230⁰C)
ASTM D1238
g/10min.
4
Tensile Strength at Yield
ASTM D638
N/mm2
37
Elongation at Yield
ASTM D638
%
27
Charpy Notched Impact Strength (at 23⁰C)
DIN 53453
mJ/mm2
4.5
Flexural Modulus (1% SECANT)
ASTM D790
MPa
1600
Rockwell Hardness
ASTM D785
R-Scale
107
Heat Distortion Temperature (Load 0.45 N/MM2)
ASTM D 648
⁰C
110
Processing Technique
Processing Temperature : 200 – 280 °C
**However, the actual processing conditions depend on mold design, power of machine, equipment and
other environments.**
Remark: The values presented on the above are typical laboratory average, not to be construed as specifications and may
vary within moderate ranges. The applicability or the accuracy of this information or the suitable of our products cannot
be guaranteed because the conditions of use on the part or our uses are beyond our control.
REV. 20110601
Product Data sheet
Mono-filament / Yarn : rope, stretch tape, coarse textile for woven bag and tarpaulin
Extrusion
: straw, sheet, industrial board
1100NK
P ol ypr op yl en e ( P P)
Description:
1100NK is a Polypropylene Homo-polymer for injection molding process with high flow
and good stiffness characteristic. It is suitable for the production of general part, long
path and thin wall, such as house-ware, closure, food container and etc. It also meets
the F.D.A. requirement in the code of federal regulations in 21 CFR 177.1520 for food
contact.
Physical Properties:
Method
Unit
Value
Melt Flow Index (2.16 kg/230⁰C)
ASTM D1238
g/10min.
11
Tensile Strength at Yield
ASTM D638
N/mm2
36
Elongation at Yield
ASTM D638
%
26
Charpy Notched Impact Strength (at 23⁰C)
DIN 53453
mJ/mm2
2.9
Flexural Modulus (1% SECANT)
ASTM D790
MPa
1500
Rockwell Hardness
ASTM D785
R-Scale
107
Heat Distortion Temperature (Load 0.45 N/MM2)
ASTM D 648
⁰C
110
Processing Temperature : 190 – 240 °C
**However, the actual processing conditions depend on mold design, power of machine, equipment and
other environments.**
Remark: The values presented on the above are typical laboratory average, not to be construed as specifications and may
vary within moderate ranges. The applicability or the accuracy of this information or the suitable of our products cannot
be guaranteed because the conditions of use on the part or our uses are beyond our control.
REV. 20110601
Product Data sheet
Processing Technique
11 75SM
P ol ypr op yl en e ( P P)
Description:
1175SM is a Homo polymer Polypropylene for extrusion coating.
It is suitable for coating woven bags and tarp aulins.
It also meets the F.D.A. requirement in the code of federal regulations in 21CFR 177.1520
Typical applications; Extrusion coating
Characteristics
; Good extrudability,Good adhesive,Good clarity,Low neck in,High speed
Physical Properties:
Method
Unit
Value
Melt Flow Index (2.16 kg/230⁰C)
ASTM D1238
g/10min.
35
Tensile Strength at Yield
ASTM D638
N/mm2
30
Elongation at Yield
ASTM D638
%
-
Charpy Notched Impact Strength (at 23⁰C)
DIN 53453
mJ/mm2
2
Flexural Modulus (1% SECANT)
ASTM D790
MPa
1200
Rockwell Hardness
ASTM D785
R-Scale
-
ASTM D 648
⁰C
100
Heat Distortion Temperature (Load 0.45 N/MM2)
Processing Temperature : 180 – 240 °C
**However, the actual processing conditions depend on machine, equipment and other environments.
Remark: The values presented on the above are typical laboratory average, not to be construed as specifications and may
vary within moderate ranges. The applicability or the accuracy of this information or the suitable of our products cannot
be guaranteed because the conditions of use on the part or our uses are beyond our control.
REV. 20110601
Product Data sheet
Processing Technique
Petrochemical Commercial Co. International Ltd. U.A.E Office
LB182202/03, Jebel Ali, Dubai
P.O.Box 261539
United Arab Emirates
HF5110 High Density Polyethylene
Tel: 00971 4 885 7724‐7
Fax: 00971 4 885 7723
Email: polymer@pccint.com
Film
Product Description
HF 5110 is a high molecular weight high density polyethylene.
Applications
HF 5110 is suitable for Extrusion, film, blown, bags and density modifies.
Typical data
Properties
Value
Unit
Test method
Density
951
kg/m3
ISO 1183
MFR (190°C/21.6kg)
10
dg/min
ISO 1133
1050
MPa
ISO527-1,2
Tensile Strength(MD)
55
MPa
ISO 527-1,3
Tensile Strength(TD)
55
MPa
ISO 527-1,3
Tensile Strain at Break(MD)
580
%
ISO 527-1
Tensile Strain at Break(TD)
620
%
ISO 527-1
Tensile Stress at Yield
26
MPa
ISO 527-1
Tensile Strain at Yield
10
%
ISO 527-1
Elemendorf tear strength(MD)
250
mN
ISO 6383-2
Elemendorf tear strength(TD)
800
mN
ISO 6383-2
Melting Point
132
°C
ISO 3146
Vicat Temp,(A50,50°C/h,10N)
127
°C
ISO 306
Tensile Modulus
The above data are typical laboratory average . They are intended to serve as guides only
Film properties taken from 20 μm blown film extruded at a melt temperature of 220°C, long stalk process, and a
blow-up ratio of 4:1.
Additive: Antioxidant – Heat stabilizer - Zinc Stearate
Producer: Arya Sasol Petrochemical Co.
Licensor: Basell
Processing
Recommended film thickness: 15 to 50 μm.
Packaging
Supplied in pellet form and can be packaged in 25Kg Bags, one ton semi bulk or 17 tons bulk
containers.
Product Data Sheet
Petrochemical Commercial Co. International Ltd. Food packaging
Handling
HF 5110 meets the relevant requirements of
plastics directive 2002/72/EC (06-08-2002) and
its amendments till directive 2008/39EC relating
to plastic materials and articles intended to come
into contact with foodstuffs.
Minimal protection to prevent possible
mechanical or thermal injury to the eyes.
Fabrication areas should be ventilated to carry
away fumes or vapors.
Combustibility
Pharmaceutical Application
HF 5110 meets the requirements of the European
pharmacopeia version 6 section 3.1.5 for
pharmaceutical application.
Conveying
Conveying equipment should be designed to
prevent accumulation of fines and dust particles
can, under certain conditions, pose an explosion
hazard. We recommend that the conveying
system used:
1. be equipped with adequate filters
2. is operated and maintained in such a manner to
ensure no leaks develop
3. that adequate grounding exists at all times
We further recommended that good
housekeeping will practiced throughout the
facility
Polyethylene resins will burn when supplied
adequate heat and oxygen. They should be
handled and stored away from contact with direct
flames and/or other ignition sources .in burning;
polyethylene resins contribute high heat and may
generate a dense black smoke. Fires can be
extinguished by conventional means with water
and mist preferred. In enclosed areas, fire fighters
should be provided with self contained breathing
apparatus.
Storage
As ultraviolet light may cause a change in the
material, all resins should be protected from
direct sunlight and/or heat during storage. The
storage location should also be dry, dust free and
the ambient temperature should not exceed 50. It
is also advisable to process polyethylene resins
(in pelletized or powder from) within 6 months
after delivery, this because also excessive aging
of polyethylene can lead to a deterioration in
quality
Note:
this information is based on our current knowledge and experience .in view of many factors
that may affect processing and application, this data does not relive processors from the
responsibility of carrying out their own tests and experiments, neither does it imply any
legally binding assurance of certain properties or of suitability for a specific purpose. It is the
responsibility of those to whom we supply our products to ensure that any proprietary rights
and existing laws and legislation are observed.
Product Data Sheet
HDPE PALLET RESIN
TAISOX HDPE 8041 Resin for Injection Molding
台塑烯 HDPE 8041 棧板專用料
棧板專用料
臺灣塑膠工業股份有限公司 聚烯事業部
台塑烯 HDPE 8041 棧板專用料
棧板專用料
一、產品描述
台塑烯 HDPE 8041 為低壓製程所生產的高密度聚乙烯。
8041 具有良好的耐衝擊強度、剛性及耐低溫脆性等特性。
8041 主要用於塑膠棧板，亦可用於大型搬運箱、運動護具、工業容器、工業用安全帽等產品。
二、基本性質
單位
檢驗方法
數值
g/10min
g/cm3
ASTM D1238
ASTM D1505
4.0
0.960
℃
台塑 DSC
133
脆化溫度
℃
ASTM D746
<-70
軟化點
機械性質
拉力降伏強度
℃
ASTM D1525
127
Kg/cm2
ASTM D638
310
拉力斷裂強度
Kg/cm2
ASTM D638
250
％
ASTM D638
1000
ASTM D790
12500
Kg-cm/cm notch
ASTM D256
8
Shore D
ASTM D2240
70
ASTM D1693
6
基本物性
熔融指數 MI2.16
密度
熱性質
熔點
拉力斷裂伸長率
彎曲模量
Kg/cm
艾式衝擊強度
硬度
2
耐環境應力龜裂
Hours
*以上資料為測試平均值，僅提供參考
三、加工建議
8041 用於一般射出成型製品時，建議加工溫度使用 180±10℃；若使用於較大型製品如棧板，
建議加工溫度使用 210±10℃。
四、法規符合
符合 FDA 21 177.1520.規定：
符合 RoHS 2011/65/EU：
符合 REACH SVHC：
符合 EU-10：
符合 EN-71：
詳細資料及證明書：
符合美國食品、藥品之包裝或容器規定
不含重金屬、PBBs 及 PBDEs
符合 151 項限用物質規定
符合歐盟食品之包裝或容器規定
符合歐盟對玩具製品重金屬含量規定
http://www2.fpc.com.tw/PE/indexc.htm
五、包裝
25Kg PE 內襯紙袋與 1 噸裝太空包。
六、儲存
於通風良好儲存溫度 40℃以下﹑無陽光直射處，可儲放 3 年。
臺灣塑膠工業股份有限公司
聚烯事業部 http://www2.fpc.com.tw/PE/indexc.htm
TAISOX HDPE 8041 Resin for Pallet
1. Product description
8041 is high density polyethylene resin made by low pressure slurry process.
8041 has good balance of stiffness and impact strength.
8041 is designed for pallets, also suitable for large crates, containers, industrial helmet etc.
2. Typical properties
Units
Test Method
Typical Value
g/10min
ASTM D1238
4.0
ASTM D1505
0.960
Properties
Melt Index MI2.16
Density
g/cm
3
Thermal properties
Melting point
℃
FPC DSC
133
Brittleness point
℃
ASTM D746
<-70
Softening point
℃
ASTM D1525
127
Mechanical properties
Tensile strength at yield
Kg/cm2
ASTM D638
250
Tensile strength at break
2
ASTM D638
310
ASTM D638
1000
ASTM D790
12500
Kg-cm/cm notch
ASTM D256
8
Shore D
ASTM D2240
70
Hours
ASTM D1693
6
Kg/cm
％
Elongation at break
Flexural Modulus
Izod Impact Strength
Hardness
Kg/cm
ESCR
2
* Data shown are average values and should not be examined for specifications
3. Processing
Taisox®8041 resin is used for general injection molding products, recommended processing temperature
180 ± 10 ℃; if used for larger products such as pallets, recommended processing temperature 210 ±
10℃.
4. Regulatory status
Meet FDA 21 177.1520.：
Meet RoHS 2011/65/EU：
Meet REACH SVHC：
Meet EU-10：
Meet EN-71：
Download from WWW：
for packaging contact with food or drug
free of heavy metal , PBBs and PBDEs
for 151 items of restricted substances
EU rules of packaging or container
EU rules of heavy metal content of toys
http://www2.fpc.com.tw/PE/indexc.htm
5. Packaging：25Kg/paper bag or 1000Kg/bulk bag.
6. Storage：Resin better be stored at temperature under 40℃.
Sun exposure, heat, humidity better avoided.
Expiration date is 3 years.
Formosa Plastics Co. Polyethylene Division
http://www2.fpc.com.tw/PE/indexc.htm