H7T30 2716 - Trelleborg Sealing Solutions

H7T30 2716 - Trelleborg Sealing Solutions

MATERIAL- DATENBLATT / MATERIAL DATA SHEET
Material-Nr.:
Material No.:
H7T30
Referenz-Material-Nr.:
Reference-Material No.:
2716
Elastomerbasis
Elastomere base
DIN ISO 1629
Härte
Hardness
DIN 53 505
Farbe
Colour
Dichte
Specific gravity
HNBR
70 ± 5 Shore A
schwarz / black
DIN EN ISO 1183-1
1,16 +/- 0,02 g/cm³
Das Material-Datenblatt befreit den Abnehmer / Anwender nicht selbst die Eignung unserer Ware für den beabsichtigten
Verwendungszweck zu prüfen. Das Datenblatt unterliegt nicht dem Änderungsdienst.
This is to emphasise that the customer himself is obliged to test the material with regard to its suitability in the
application. This data sheet has not a change of service.
Polymer Laboratory Stuttgart
erstellt am / issued:
Fax.: +49 711 7864 778
TSS.PolymerLaboratoryStuttgart@trelleborg.com
Unterschrift / signature:
2007-06-06
kfu
FB-PLS-001/f2007-04-02 Vers.4 kfu
MATERIAL- DATENBLATT / MATERIAL DATA SHEET
Material-Nr.:
Material No.:
H7T30
November 1996
DATA SHEET
MATERIAL REFERENCE No. 2716
Hardness Range : 65 - 75 IRHD
Dowty Automotive (Malta) Ltd. material reference 2716 is based on a Hydrogenated Nitrile (HNBR)
polymer specifically designed to have the maximum heat resistance possible with this class of elastomers.
Compound Key Properties include :
-
High mechanical properties.
Good heat resistance.
Resistant to mineral oils.
Good resistance to hot water.
Good resistance to ozone and weathering.
Resistant to refrigerants (R12/R134a) and lubricant oils, ( Mineral oil /PAG)
Projected service temperature range of -30 to +150°C which is dependant upon medium
to be sealed and conditions of service.
Applications :
-
Hydraulic and pneumatic.
Cooling/Heating systems.
Air Conditioning ( R134a /PAG)
Under bonnet / engine.
The information herein is accurate to the extent of our current technical knowledge. Dowty Automotive (Malta) Ltd. makes no
warranty that the material is suitable for all applications. Customers should undertake their own tests to ensure suitability for
particular conditions of operation.
Polymer Laboratory Stuttgart
erstellt am / issued:
Fax.: +49 711 7864 778
TSS.PolymerLaboratoryStuttgart@trelleborg.com
Unterschrift / signature:
2007-06-06
gäb
FB-PLS-001/f2007-04-02 Vers.4 kfu
MATERIAL- DATENBLATT / MATERIAL DATA SHEET
Material-Nr.:
Material No.:
H7T30
MATERIAL REFERENCE No. 2716
CLAUSES
UNITS
SPECIFICATION
Hardness
Tensile Strength
Elongation @ Break
IRHD
N/mm2
%
70 +/-5
18.0 min.
250 min.
Compression Set :
24 hrs @ 150°C
%
20.0 max.
IRHD
%
%
+5 max
+/-10
+/-10
IRHD
%
+/-5
+/-5
Hardness Change
Volume Change
IRHD
%
0 to -10
0 to +15
Low Temperature Retraction :
TR 10
°C
-19 min.
Physical Properties :
Air Ageing :
70 hrs @ 150°C
Hardness Change
Tensile Change
Elongation Change
Fluid Resistance :ASTM No 1
70 hrs @ 150°C
Hardness Change
Volume Change
Fluid Resistance :ASTM No. 2
70 hrs @ 150°C
Note : 1) All tests were carried out on 2mm test sheets, except for compression set (buttons).
2) All tests carried out to ASTM procedure.
Polymer Laboratory Stuttgart